Inspectable black glass containers

ABSTRACT

A soda-lime-silica glass container and related methods of manufacturing. A black-strikable glass composition having a base glass portion and a latent colorant portion is prepared. The base glass portion includes soda-lime-silica glass materials and one or more blue colorant materials, and the latent colorant portion includes cuprous oxide (Cu 2 O), stannous oxide (SnO), bismuth oxide (Bi 2 O 3 ), and carbon (C). Glass containers may be formed from the black-strikable glass composition, and these glass containers may be heated to a temperature greater than 600 degrees Celsius to strike black therein. The glass containers formed from the black-strikable glass composition may be inspected—before or after striking—by infrared inspection equipment.

The present disclosure is directed to glass containers and, more particularly, to coloring of glass containers.

BACKGROUND AND SUMMARY OF THE DISCLOSURE

Glass containers are often composed of so-called soda-lime glass, also called soda-lime-silica glass. Many such containers are colored, for example, for aesthetic or functional purposes. Colored glass containers may be produced from soda-lime glass compositions which include one or more colorants. For example, blue glass containers can be made from soda-lime glass compositions which include cobalt oxide (CoO) as a colorant. U.S. patents that illustrate colored glass compositions of this type include U.S. Pat. No. 3,326,702, U.S. Pat. No. 3,330,638, U.S. Pat. No. 3,345,190, U.S. Pat. No. 3,498,806, and U.S. Pat. No. 4,312,953.

Some colorants in soda-lime glass do not immediately impart color to the glass. Instead, color may need to be developed in the colorant-containing glass by a heat-treatment process known as “striking.” In this process, glass containers are formed from a glass composition which contains “latent” colorants. Thereafter, the glass containers are heated to a temperature slightly above normal annealing temperatures so that the latent colorants in the glass interact or “strike” to impart color to the glass. U.S. Patents that illustrate this method of coloring glass containers include U.S. Pat. No. 2,672,423, U.S. Pat. No. 3,513,003, and/or U.S. Pat. No. 3,627,548.

A general object, in accordance with one aspect of the disclosure, is to provide a glass composition that may be used to produce cobalt blue glass containers that, upon heat treatment and striking, develop a visually black color. Accordingly, this glass composition and the glass containers formed therefrom may be referred to as “black-strikable.” The glass containers may be inspected—before or after striking—by infrared inspection equipment in a glass container production line or in a container filling operation. Accordingly, these glass containers also may be referred to as “inspectable.” Until now, the optical inspection of black glass containers had been thought impossible due to their low percentage of light transmission.

The present disclosure embodies a number of aspects that can be implemented separately from or in combination with each other.

In accordance with an aspect of the disclosure, there is provided a method of making a black-strikable glass container. In this method, a black-strikable glass composition is prepared having a base glass portion and a latent colorant portion. The base glass portion includes: 60-75 wt. % SiO₂, 7-15 wt % Na₂O, 6-12 wt, % CaO, 0.1-3.0 wt. % Al₂O₃, 0.0-2.0 wt. % MgO, 0.0-2.0 wt. % K₂O, 0.01-0.25 wt. % SO₃, 0.01-0.25 wt. % Fe₂O₃, and 0.01-0.15 wt. % CoO. The latent colorant portion includes: 0.0875-0.35 wt. % cuprous oxide (Cu₂O), 0.06-0.5 wt. % stannous oxide (SnO), 0.006-0.05 wt. % bismuth oxide (Bi₂O₃), and 0.02-0.10 wt. % carbon (C). Thereafter, a black-strikable glass container is formed from the black-strikable glass composition.

In accordance with another aspect of the disclosure, there is provided a method of inspecting a black glass container for commercial variations that affect optical characteristics of the glass container. In this method, infrared light energy is directed onto and through the black glass container, and is received on an infrared light sensor. The infrared light sensor is responsive to infrared light energy received thereon having wavelengths in the range of 750-1100 nm.

BRIEF DESCRIPTION OF THE DRAWINGS

The disclosure, together with additional objects, features, advantages and aspects thereof, will be best understood from the following description, the appended claims and the accompanying drawings, in which:

FIG. 1 is a side elevation of a glass container in accordance with an exemplary embodiment of the present disclosure; and

FIG. 2 is a graphical plot of light transmission through samples of inspectable struck-black container glass doped with three different amounts of copper oxide (Cu₂O).

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

FIG. 1 illustrates an exemplary embodiment of a glass container 10 (e.g., glass bottle, jar, or the like) that may be produced in accordance with an exemplary embodiment of a presently disclosed manufacturing process, as described further herein below. The glass container 10 may be referred to as “inspectable,” meaning that the glass container 10 transmits a sufficient amount of infrared light to be inspected by infrared inspection equipment in a glass container production line or in a container filling operation.

The glass container 10 may be produced by the following method. Additional exemplary conditions and procedures for composing and melting production container glass can be found in, e.g. the Handbook of Glass Manufacture by Fay V. Tooley (3rd ed., Ashlee Publishing 1984).

The method may include preparing a black-strikable glass composition. The black-strikable glass composition may be thought of as having a base glass portion and a latent colorant portion.

The base glass portion may include soda-lime-silica glass materials and one or more blue colorant materials. For example, the base glass portion may include substantially the same materials present in cobalt blue glass.

The term “cobalt blue glass” is employed in its conventional sense in glass technology as referring to a glass having blue coloration (e.g., blue glass). A presently preferred cobalt blue glass may comprise the following materials in the following ranges of amounts by weight:

60-75% SiO₂  7-15% Na₂O  6-12% CaO 0.1-3.0% Al₂O₃ 0.0-2.0% MgO 0.0-2.0% K₂O 0.01-0.25% SO₃ 0.01-0.25% Fe₂O₃ 0.01-0.15% CoO.

More particularly, and by way of example only, a presently preferred cobalt blue glass may comprise the following materials in substantially the stated amounts by weight:

  73% SiO₂   13% Na₂O   11% CaO  1.6% Al₂O₃  0.5% MgO  0.4% K₂O 0.15% SO₃ 0.10% Fe₂O₃ 0.06% CoO.

The latent colorant portion of the black-strikable glass composition may include cuprous oxide (Cu₂O), stannous oxide (SnO), bismuth oxide (Bi₂O₃), and carbon (C), as this combination of materials has been found to enable the striking of copper (Cu) in soda-lime glass containers.

The molar ratio of tin oxide (SnO) to copper oxide (Cu₂O) in the latent colorant portion may be about one, for example, the molar ratio may be in the range of 0.9 to 1, or in the range of about 1 to 0.9. However, the latent colorant portion suitably may contain an excess of tin oxide (SnO). For example, when an excess of tin oxide (SnO) is present in the latent colorant portion, the molar ratio of tin oxide (SnO) to copper oxide (Cu₂O) may be about 1.5.

In one embodiment, the black-strikable glass composition may include about 0.175 wt. % cuprous oxide (Cu₂O), about 0.25 wt. % stannous oxide (SnO), about 0.0125 wt. % bismuth oxide (Bi₂O₃), and about 0.06 wt. % carbon (C). For example, the black-strikable glass composition may include 0.0875-0.35 wt. % cuprous oxide (Cu₂O), 0.06-0.5 wt. % stannous oxide (SnO), 0.006-0.05 wt. % bismuth oxide (Bi₂O₃), and 0.02-0.10 wt. % carbon (C). In another embodiment, the black-strikable glass composition may include substantially 0.175 wt. % cuprous oxide (Cu₂O), substantially 0.25 wt. % stannous oxide (SnO), substantially 0.0125 wt. % bismuth oxide (Bi₂O₃), and substantially 0.06 wt. % carbon (C). As used herein the term “substantially” means within manufacturing tolerances customary in the glass container manufacturing industry.

The remaining portion of black-strikable glass composition may include small amounts of other materials. Such materials may be additives, residual materials from cullet, and/or impurities typical in the glass container manufacturing industry. Such materials may be present in trace amounts, for example, less than 0.2 wt. %. In one specific example, the remaining portion of the black-strikable glass composition may include trace amounts of TiO₂, BaO, and/or SrO.

The method also may include forming black-strikable glass containers from the black-strikable glass composition. A feeder located at a downstream end of the one or more forehearths may be used to measure out gobs of molten glass and to deliver them to glass container-forming machines. Thereafter, the gobs may be formed into glass containers, for example, by press-and-blow or blow-and-blow processes and by individual section machines, or in any other suitable manner by any suitable equipment.

The method further may include annealing the black-strikable glass containers in any suitable manner, for example, in an annealing lehr. At an entry, hot end, or upstream portion of the annealing lehr, the temperature therein may be between 550 and 600 degrees Celsius. Through the lehr, the temperature may be brought down gradually to a downstream portion, cool end, or exit of the lehr, for example, to a temperature therein of between 130 degrees Celsius and 65 degrees Celsius. In any event, the glass containers may be annealed, preferably between 550 and 600 degrees Celsius for 30 to 90 minutes, more preferably between 525 and 575 degrees Celsius for 45 to 75 minutes, and most preferably at substantially 550 degrees Celsius for one hour.

The method also may include raising the temperature of the black-strikable glass containers above the highest temperature at which they are annealed (i.e., the highest annealing temperature) to strike black coloration into the glass containers. Accordingly, this temperature-raising step may be referred to as “striking.”

The striking or temperature-raising step may include, for example, heat-treating the glass containers between 600 and 680 degrees Celsius for 10 to 90 minutes to produce black glass containers. In a more specific example, the temperature-raising step may include heat-treating the black-strikable glass containers between 630 and 650 degrees Celsius for 30 to 40 minutes.

In one embodiment, the temperature raising or striking step may be carried out after the annealing step. For example, a furnace or secondary lehr may be used in line or off line downstream of the annealing lehr. The temperature of the glass containers may be raised in the furnace or secondary lehr to a temperature and for a time suitable to strike black into the glass containers. Thereafter, the temperature of the black glass containers may be brought down gradually, for example, according to an annealing schedule to avoid fracture or failure of the containers.

In another embodiment, the temperature raising or striking step may be carried out between the time the annealing step begins and the time the annealing step ends. In one example, a separate furnace may be used off line adjacent to the annealing lehr. In another example, the annealing lehr may be operated in accordance with a modified heating profile. For instance, the modified heating profile may include a typical annealing temperature profile modified to include temperatures and times suitable to strike black into the glass containers before, during, or after annealing.

The black-strikable glass containers may, in some respects, have a container glass composition that is different from the black-strikable glass composition. For example, the amount of sulfur trioxide (SO₃) retained in the glass containers may be substantially less than the amount of sulfur trioxide (SO₃) in the black-strikable glass composition. The actual amount of sulfur trioxide (SO₃) retained in the glass containers will vary depending on the amount of carbon (C) in the black-strikable glass composition. In suitable embodiments, the amount of sulfur trioxide (SO₃) retained in the glass containers will be in the range of 0.01 to 0.22 wt. %. In general, the more carbon (C) in the black-strikable glass composition, the less sulfur trioxide (SO₃) will be retained in the glass containers. As another example, the latent colorant materials of Cu₂O, SnO, and Bi₂O₃ may be largely retained in the container glass composition. For example, about 75-100% of the Cu₂O, SnO, and Bi₂O₃ in the black-strikable glass composition may be retained in the container glass composition.

A struck-black glass container produced in accordance with this disclosure may have a wall thickness of greater than 0.040 inches (i.e., greater than about 1 mm). At this wall thickness, the glass container transmits a minimal amount of light at wavelengths between 390 nm and 700 nm and, thus, appears visually black to the human eye in natural lighting conditions (e.g., indirect sunlight) at arm's length. For example, a struck-black glass container produced in accordance with this disclosure may transmit light in an amount less than 10% at wavelengths between 390 nm and 675 nm.

At the same time, a struck-black glass container produced in accordance with this disclosure transmits infrared light in the near-infrared region of the electromagnetic spectrum (e.g., from about 750 nm to 1100 nm) and, thus, may be inspected by infrared inspection equipment in a glass container production line or in a container filling operation. For example, a struck-black glass container produced in accordance with this disclosure may transmit light in an amount between about 30% and about 65% at wavelengths between 750 nm and 850 nm. In one specific example, a struck-black glass container produced in accordance with this disclosure may transmit light in an amount of at least 40% at a wavelength of 750 nm.

Glass containers produced in accordance with this disclosure may be inspected—either before or after striking—to detect for commercial variations in the glass. Such commercial variations may include, for example, dimensional anomalies in the sidewalls, heels, bottoms, shoulders, and/or necks of the glass containers, as well as inhomogeneities in the glass itself that affect the optical properties of the glass containers. Some of these commercial variations may be within commercially acceptable standards or thresholds, while other variations may be outside of such standards or thresholds, and thus may be unacceptable.

A suitable apparatus for detection of commercial variations in a glass container produced in accordance with this disclosure includes a light source, a light receiver, and an information processor. The light source may include a lamp or a laser capable of emitting infrared light in the near-infrared region of the electromagnetic spectrum (e.g., from about 750 nm to 1100 nm), and the light receiver may include a laser optic sensor responsive to light energy at wavelengths in the range of about 750 nm to 1100 nm.

A glass container produced in accordance with this disclosure may be inspected by directing light energy from an infrared light source through the glass container and onto a light sensor. In one embodiment, infrared light in the near-infrared region of the electromagnetic spectrum may be directed through the glass container and onto the light sensor. In another embodiment, infrared light at wavelengths in the range of about 750-850 nm may be directed through the glass container and onto the light sensor. In response, the light sensor may provide electrical signals to an information processor, which may analyze the electrical signals to determine whether the glass container is commercially acceptable or unacceptable. Before the present discovery, no known commercially available black glass containers were believed to be capable of inspection using an infrared light source.

According to the present disclosure, a black-strikable glass composition is provided that may be used to produce cobalt blue glass containers and optionally black glass containers by the process of “striking.” In addition, the glass containers produced according to the present disclosure may be inspected—before or after striking—by infrared inspection equipment in a glass container production line or in a container filling operation.

Several glass test samples were prepared in a laboratory environment and color was observed in each sample.

Example 1

In the following example, a batch of raw materials was prepared and used to produce 300 g of molten glass. The batch of raw materials included the necessary raw materials to produce a black-strikable glass composition. The necessary amount of each raw material for the batch was weighted out in accordance with standard batch calculation practice common in the glass industry. Thereafter, the raw materials were crashed and ground using a mortar and pestle to break up agglomerate material, and then mixed together using a mixer for about ten minutes. While mixing, a crucible was pre-heated in a furnace at 1350 degrees Celsius for about ten minutes. The crucible was removed from the furnace and the entire batch of raw materials was added to the crucible. The crucible was again placed in the furnace, and the temperature of the furnace was increased to form a glass melt having a temperature of about 1450 degrees Celsius. The glass melt was held at that temperature for about 3.5 hours.

Thereafter, the molten glass was poured into splat quenched patties. Some of the patties were placed in an annealing oven at 550 degrees Celsius, and some of the patties were left unannealed. The patties which were placed in the annealing oven were annealed at a temperature of about 550 degrees Celsius for about 10 to 20 minutes, and then a door of the annealing oven was cracked open until the annealing oven temperature decreased to a temperature of about 300 degrees Celsius. Thereafter, the annealing oven temperature was set to 20 degrees Celsius to let the glass cool down to room temperature overnight.

After the black-strikable glass patties were annealed, they were heat treated at oven temperatures of 550, 600, and 650 degrees Celsius for durations of 15 to 90 minutes. At 600 and 650 degrees Celsius, the samples struck black by 30 minutes.

FIG. 2 illustrates three plots of Transmission (%) vs. Wavelength (nm) through samples of cobalt blue glass doped with suitable amounts of the disclosed latent colorant materials. However, each of the samples was doped with a different amount of copper oxide (Cu₂O). The three plots illustrate samples doped with 0.12 wt. % Cu₂O (dash dot), 0.15 wt. % Cu₂O (dashed), and 0.175 wt. % Cu₂O (solid), respectively. As shown, these struck-black samples exhibit 0% to 5% transmission at wavelengths between 200 nm and 390 nm (ultraviolet light), 0% to 10% transmission at wavelengths between 390 nm and 675 nm (visible light), and 30% to 65% transmission at wavelengths between 750 nm and 850 nm (infrared light). Therefore, a struck-black glass container formed by doping a cobalt blue glass with suitable amounts of the disclosed latent colorant materials transmits a sufficient amount of infrared light so as to be inspected by infrared inspection equipment.

There thus has been disclosed suitable methods of producing a black-strikable glass composition and black-strikable glass containers that folly satisfy all of the objects and aims previously set forth. The disclosure has been presented in conjunction with several exemplary embodiments, and additional modifications and variations have been discussed. Other modifications and variations readily will suggest themselves to persons of ordinary skill in the art in view of the foregoing discussion. The disclosure is intended to embrace all such modifications and variations as fall within the spirit and broad scope of the appended claims. 

The invention claimed is:
 1. A method of making glass containers including the steps of: preparing a black-strikable glass composition formulated to produce blue glass, which upon heat treatment and striking, develops a visually black color, the black-strikable glass composition having a base glass portion and a latent colorant portion, the base glass portion including 60-75 wt. % SiO₂, 7-15 wt. % Na₂O, 6-12 wt. % CaO, 0.1-3.0 wt. % Al₂O₃, 0.0-2.0 wt. % MgO, 0.0-2.0 wt. % K₂O, 0.01-0.25 wt. % SO₃, 0.01-0.25 wt. % Fe₂O₃, and 0.01-0.15 wt. % CoO and the latent colorant portion including 0.0875-0.35 wt. % cuprous oxide (Cu₂O), 0.06-0.5 wt. % stannous oxide (SnO), 0.006-0.05 wt. % bismuth oxide (Bi₂O₃), and 0.02-0.10 wt. % carbon (C); and forming a plurality of glass containers from the black-strikable glass composition, wherein the plurality of glass containers can be struck black to produce a plurality of black glass containers that transmit 30% to 65% infrared light so as to be inspectable using an infrared light source.
 2. The method set forth in claim 1 including the additional step of: raising the temperature of the plurality of glass containers above 600 degrees Celsius to strike black coloration into the glass containers to produce a plurality of black glass containers.
 3. The method set forth in claim 2 wherein the temperature of the plurality of glass containers is raised above 600 degrees Celsius for 10 to 90 minutes to produce the plurality of black glass containers.
 4. A black glass container produced by the method set forth in claim
 2. 5. The method as set forth in claim 2 wherein the plurality of black glass containers have a transmittance of less than 10% to light having wavelengths between 390 nm and 675 nm and a transmittance of greater than 30% to light having wavelengths between 750 nm and 850 nm.
 6. The method as set forth in claim 5 wherein the plurality of black glass containers have a transmittance of at least 40% to light having a wavelength of 750 nm.
 7. The method set forth in claim 1 including the additional step of: raising the temperature of the plurality of glass containers to a temperature between 630 degrees Celsius and 650 degrees Celsius to strike black coloration into the glass containers to produce a plurality of black glass containers.
 8. The method set forth in claim 7 wherein the temperature of the plurality of glass containers is raised to a temperature between 630 degrees Celsius and 650 degrees Celsius for 30 to 40 minutes to produce the plurality of black glass containers.
 9. The method as set forth in claim 1 wherein the amount of sulfur trioxide (SO₃) retained in the plurality of glass containers is in the range of 0.01-0.22 wt. %.
 10. The method as set forth in claim 1 wherein the temperature of the plurality of glass containers is not raised above 600 degrees Celsius after formation and the color of the glass containers is blue.
 11. The method set forth in claim 1 including the additional steps of: raising the temperature of a first portion of the plurality of glass containers above 600 degrees Celsius to strike black coloration into the first portion of the glass containers to produce a plurality of black glass containers; and maintaining a remaining portion of the plurality of glass containers at a temperature below 600 degrees Celsius after forming such that the remaining portion of the glass containers are blue.
 12. A plurality of black glass containers produced by the method set forth in claim
 11. 13. The method set forth in claim 1 wherein the latent colorant portion of the black-strikable glass composition enables the striking of copper (Cu) in the plurality of glass containers when the temperature of the plurality of glass containers is raised above 600 degrees Celsius.
 14. A method of making glass containers including the steps of: preparing a black-strikable glass composition formulated to produce blue glass, which upon heat treatment and striking, develops a visually black color; forming a plurality of glass containers from the black-strikable glass composition; raising the temperature of a first portion of the plurality of glass containers above 600 degrees Celsius to strike black coloration into the first portion of the glass containers to produce a plurality of black glass containers; and maintaining a remaining portion of the plurality of glass containers at a temperature below 600 degrees Celsius after forming such that the remaining portion of the glass containers are blue, wherein the plurality of black glass containers transmit 30% to 65% infrared light so as to be inspectable using an infrared light source.
 15. The method as set forth in claim 14 wherein the black-strikable glass composition comprises 0.01-0.15 wt. % cobalt oxide (CoO), 0.0875-0.35 wt. % cuprous oxide (Cu₂O), 0.06-0.5 wt. % stannous oxide (SnO), 0.006-0.05 wt. % bismuth oxide (Bi₂O₃), and 0.02-0.10 wt. % carbon (C).
 16. The method as set forth in claim 14 wherein the plurality of glass containers include a retained amount of sulfur trioxide (SO₃) in the range of 0.01-0.22 wt. %.
 17. The method as set forth in claim 14 wherein the plurality of black glass containers have a transmittance of less than 10% to light having wavelengths between 390 nm and 675 nm and a transmittance of greater than 30% to light having wavelengths between 750 nm and 850 nm.
 18. The method as set forth in claim 14 wherein the black-strikable glass composition comprises 60-75 wt. % SiO₂, 7-15 wt. % Na₂O, 6-12 wt. % CaO, 0.1-3.0 wt. % Al₂O₃, 0.0-2.0 wt. % MgO, 0.0-2.0 wt. % K₂O, 0.01-0.25 wt. % SO₃, and 0.01-0.25 wt. % Fe₂O₃. 